How to draft an AWS D1.1:2025 Welding Procedure Specification for Gas Metal Arc Welding (GMAW) on ASTM A588 Weathering Steel. Recommended filler: ER80S-W. Below: process notes, base metal properties, prequalification path, typical parameters, and which essential variables to watch.
About GMAW (Gas Metal Arc Welding)
Solid-wire continuous-feed process with external shielding gas (typically 75/25 Ar/CO₂ or 90/10 Ar/CO₂). Constant voltage (CV) output and a fixed wire feed speed give a stable arc. Transfer mode (short-circuit, globular, spray, pulsed) is selected by voltage + current combination. Note: A5.36 was dropped from the AWS D1.1:2025 Table 6.6 allowed-spec list for GMAW.
Process family: semi-auto. Suited to: shop fabrication of structural members, high-deposition shop welds, and similar work.
About ASTM A588
Atmospheric corrosion-resistant (weathering) HSLA steel. The Cor-Ten family. Used unpainted; develops a stable oxide layer. Filler metal must be color-matched (weathering grade) or the joint must be painted.
- AWS D1.1 Group (Table 6.9)
- Group I
- Yield (ksi)
- 50
- Tensile (ksi)
- 70
- Weldability
- good
Prequalification path
ASTM A588 (Group I) is on the prequalified base metals list for GMAW per AWS D1.1:2025 Clause 5. A written WPS is still mandatory but no PQR test is required as long as every Clause 5 essential variable (joint geometry, filler, preheat, current/polarity, etc.) is met.
Preheat: 70°F up to 3/4 in; 200°F from 3/4 in to 1-1/2 in; 300°F above 1-1/2 in for low-hydrogen practice. Filler must match weathering chemistry (e.g., E8018-W, ER80S-W).
Typical parameters
Starting points only. Verify against electrode manufacturer data and your PQR.
| Filler | ER80S-W |
| Amperage | 150–280 A (0.045 in wire) |
| Voltage | 22–28 V (spray transfer) |
| Travel speed | 10–25 ipm |
| Position(s) typically qualified | All positions (1G–4G); 5G/6G for pipe per Clause 10 |
Essential variables to watch (AWS D1.1:2025 Table 6.6)
If your shop is working from a PQR, these are the GMAW-specific changes that require requalification per Table 6.6. The rule engine flags every one of them with the row number, clause reference, and the actual delta.
- Shielding gas composition (any change)
- Voltage > 7% change
- Amperage > 10% change
- Wire diameter increase
- Transfer mode change (short-circuit ↔ spray ↔ pulsed)
- CV ↔ CC output change
A588 weathering steel: the filler metal must color-match (e.g., E8018-W, ER80S-W) unless the joint is painted. A non-weathering filler is a Table 6.6 row 3 essential variable change if it deviates from PQR.
Where GMAW on ASTM A588 fits
- Highway bridges (unpainted)
- Exposed architectural structures
- Outdoor sculptures
- Industrial buildings without painted finish
Start now
Draft this WPS in the next 2 minutes.
Start a 14-day Pro trial and the editor opens with this GMAW + ASTM A588 setup preselected. AI drafts every narrative section with inline citations to AWS D1.1:2025. Export as a PDF, your CWI signs.
Related WPS templates
FAQ
Does AWS D1.1:2025 prequalify GMAW on ASTM A588?
Yes — ASTM A588 is on the Clause 5 prequalified base metals list and GMAW is a Clause 5 prequalified process. You still need a written WPS but no PQR.
What filler is recommended for GMAW on ASTM A588?
ER80S-W. Verify against your project specification and the consumable manufacturer's data sheet. Filler classification change is a Table 6.6 essential variable.
What preheat does ASTM A588 need?
70°F up to 3/4 in; 200°F from 3/4 in to 1-1/2 in; 300°F above 1-1/2 in for low-hydrogen practice. Filler must match weathering chemistry (e.g., E8018-W, ER80S-W).